Specifications:AISI 304/304L,ASTM A240, AMS 5513/5511
·Finishes: 2B Mill (dull), #4 Brushed (appliances), #8 Mirror
·Applications: sanitary dairy, beverage and food product handling and processing, hospital equipment, marine hardware, kitchen appliances, back splashes, etc.
·Workability:Easy to Weld, Cut, Form and Machine with proper equipment
·Mechanical Properties: Nonmagnetic,Tensile = 85,000 +/-, Yield = 34,000 +/-, Brinell = 170
·How is it Measured?thickness X width X length
·Available Stock Sizes:1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size
C% | Si% |
Mn% |
P% |
S% |
Cr% |
Ni% |
N% |
Mo% |
Cu% |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
18.0-20.0 |
8.0-10.0 |
-- |
- |
-- |
T*S |
Y*S |
Hardness |
Elongation |
|
(Mpa) |
(Mpa) |
HRB |
HB |
(%) |
≥520 |
≥205 |
-- |
-- |
≥40 |
Description of 304 Stainless Steel Coil
Product |
Stainless Steel Coil 2B NO.1 finish |
Material Type |
stainless steel, nonmagnetic. |
Material Origin |
SASA METAL,TISCO, BAOSTEEL, JISCO,POSCO |
Grade |
200series,300series,400series |
Technology |
Cold Rolling & Hot Rolling |
Thickness |
0.1mm to 100mm |
Width |
600mm to 2500mm |
Length |
1219x2440mm (4‘x8’), 1250x2500mm,1500*6000mm or any other customized size |
Surface |
BA, 2B, 2D, 4K, 6K, 8K, NO.4, HL, SB, Embossed |
Edge |
Mill Edge, Slit Edge |
Other Choices |
Leveling: improve flatness, esp. for items with high flatness request. |
Skin-Pass: improve flatness, higher brightness | |
Strip Slitting: any width from 10mm to 200mm | |
Sheets Cutting: Square Sheets, Retangle Sheets, Circles, Other Shapes | |
Protection |
1. Inter paper available |
2. PVC protecting film available | |
Packing |
Water-proof paper + Edge Protection + Wooden Pallets |
Production Time |
20-45 days depending on processing requirement & business season |
Payment Term |
T/T, Irrevocable L/C at sight |
Surface of SS 304 coil
Surface Finish |
Definition |
Application |
2B |
Those finished, after cold rolling, by heat treatment, pickling or other equivalent treatment and lastly by cold rolling to given appropriate luster. |
Medical equipment, Food industry, Construction material, Kitchen utensils. |
BA |
Those processed with bright heat treatment after cold rolling. |
Kitchen utensils, Electric equipment, Building construction. |
NO.3 |
Those finished by polishing with No.100 to No.120 abrasives specified in JIS R6001. |
Kitchen utensils, Building construction. |
NO.4 |
Those finished by polishing with No.150 to No.180 abrasives specified in JIS R6001. |
Kitchen utensils, Building construction, Medical equipment. |
HL |
Those finished polishing so as to give continuous polishing streaks by using abrasive of suitable grain size. |
Building Construction. |
NO.1 |
The surface finished by heat treatment and pickling or processes corresponding there to after hot rolling. |
Chemical tank, pipe. |
More grades of Stainless Coil
Type |
Grade |
Grade |
Chemical Component % |
||||
Austenitic stainless steel |
C |
Cr |
Ni |
Mn |
|||
201 |
1Cr17Mn6Ni5N |
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
||
201L |
03Cr17Mn6Ni5N |
≤0.030 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
||
202 |
1Cr18Mn8Ni5N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
||
204 |
03Cr16Mn8Ni2N |
≤0.030 |
15.00-17.00 |
1.50-3.50 |
7.00-9.00 |
||
1Cr18Mn10Ni5Mo3N |
≤0.10 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|||
2Cr13Mn9Ni4 |
0.15-0.25 |
12.00-14.00 |
3.70-5.00 |
8.00-10.00 |
|||
2Cr15Mn15Ni2N |
0.15-0.25 |
14.00-16.00 |
1.50-3.00 |
14.00-16.00 |
|||
1Cr18Mn10Ni5Mo3N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|||
301 |
1Cr17Ni7 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
||
302 |
1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
303 |
Y1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
303se |
Y1Cr18Ni9Se |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
304 |
0Cr18Ni9 |
≤0.07 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
304L |
00Cr19Ni10 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
||
304N1 |
0Cr19Ni9N |
≤0.08 |
18.00-20.00 |
7.00-10.50 |
≤2.00 |
||
304N2 |
0Cr18Ni10NbN |
≤0.08 |
18.00-20.00 |
7.50-10.50 |
≤2.00 |
||
304LN |
00Cr18Ni10N |
≤0.030 |
17.00-19.00 |
8.50-11.50 |
≤2.00 |
||
305 |
1Cr18Ni12 |
≤0.12 |
17.00-19.00 |
10.50-13.00 |
≤2.00 |
||
309S |
0Cr23Ni13 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
||
310S |
0Cr25Ni20 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
||
316 |
0Cr17Ni12Mo2 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
||
1Cr18Ni12Mo2Ti6) |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
0Cr18Ni12Mo2Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
316L |
00Cr17Ni14Mo2 |
≤0.030 |
16.00-18.00 |
12.00-15.00 |
≤2.00 |
||
316N |
0Cr17Ni12Mo2N |
≤0.08 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
||
316N |
00Cr17Ni13Mo2N |
≤0.030 |
16.00-18.50 |
10.50-14.50 |
≤2.00 |
||
316J1 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
17.00-19.00 |
10.00-14.50 |
≤2.00 |
||
316J1L |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
17.00-19.00 |
12.00-16.00 |
≤2.00 |
||
317 |
0Cr19Ni13Mo3 |
≤0.12 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
||
317L |
00Cr19Ni13Mo3 |
≤0.08 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
||
1Cr18Ni12Mo3Ti6 |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
0Cr18Ni12Mo3Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
317J1 |
0Cr18Ni16Mo5 |
≤0.040 |
16.00-19.00 |
15.00-17.00 |
≤2.00 |
||
321 |
1Cr18Ni9Ti6 |
≤0.12 |
17.00-19.00 |
8.00-11.00 |
≤2.00 |
||
0Cr18Ni10Ti |
≤0.08 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
|||
347 |
0Cr18Ni11Nb |
≤0.08 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
||
XM7 |
0Cr18Ni9Cu3 |
≤0.08 |
17.00-19.00 |
8.50-10.50 |
≤2.00 |
||
XM15J1 |
0Cr18Ni13Si4 |
≤0.08 |
15.00-20.00 |
11.50-15.00 |
≤2.00 |
Austenite |
329J1 |
0Cr26Ni5Mo2 |
≤0.08 |
23.00-28.00 |
3.00-6.00 |
≤1.50 |
≤0.035 |
≤0.030 |
1.00-3.00 |
≤1.00 |
- |
- |
2) |
1Cr18Ni11Si4AlTi |
0.10-0.18 |
17.50-19.50 |
10.--120.. |
≤0.80 |
≤0.035 |
≤0.030 |
- |
3.40-4.00 |
- |
- |
Al 0.10-0.30; Ti 0.40-0.70 |
||
00Cr18Ni5MoSi2 |
≤0.030 |
18.00-19.50 |
4.50-5.50 |
1.00-2.00 |